Technical Data Sheet
NATPET polypropylene grades for healthcare applications are produced under controlled conditions to ensure consistent quality and contamination free resins.
H12ML-MG is a Homopolymer for injection molding application. Produced using Spheripol® technology, the grade has an exceptional advantage of having morphologically uniform resins, medium flow ability and high stiffness.
It is recommended that all potential activities for applications of this grade in the healthcare area have to be discussed with the relevant technical and business representative of NATPET particularly for use of this product in an implantable device that is introduced into the human body by surgical intervention and is intended to remain in place following surgical procedure.
|Melt Flow Rate (MFR)||230°C/2.16 kg||ASTM 1238-13||12||g/10-min|
|Flexural Modulus||ISO 178||1,500||MPa|
|Tensile Modulus||1-mm/min||ISO 527||1,550||MPa|
|Tensile Stress at Break||50-mm/min||ISO 527||26||MPa|
|Tensile Strain at Yield||50-mm/min||ISO 527||35||MPa|
|Tensile Strain at Break||50-mm/min||ISO 527||> 50||%|
|Tensile Strain at Yield||50-mm/min||ISO 527||13||%|
|Izod Notched||23°C||ISO 180||3.9||kJ/m2|
|Heat Deflection Temperature||0.45 MPa Un-annealed||ISO 75B||91||°C|
|Vicat Softening Temperature||A50 (50°C/h 10N)||ISO 306||152||°C|
|Note: The above are typical data representing the product; not to be construed as analysis certificate or specifications.|