Teldene® H06ML

Technical Data Sheet
Typical Applications
• Used for the production of consumer goods such as food containers, house wares, toys and garden furniture
• Components for appliances and parts for the automotive industry

Key Characteristics
• Good flow properties, High Stiffness, easy processing
• Food contact approval for specific applications (refer to NATPET)

Processing Method
• Injection Molding

Density23°CISO 11830.900g/cm3
Melt Flow Rate (MFR)230°C/2.16 kgASTM 1238-136.0g/10-min
Flexural ModulusISO 1781,500MPa
Tensile Stress at Break50-mm/minISO 52724MPa
Tensile Stress at Yield50-mm/minISO 52734MPa
Tensile Strain at Break50-mm/minISO 527> 50%
Tensile Strain at Yield50-mm/minISO 52713%
Izod Notched23°CISO 180
Heat Deflection Temperature0.45 MPa Un-annealedISO 75B115°C
Vicat Softening TemperatureA50 (50°C/h 10N)ISO 306155°C
Note: The above are typical data representing the product; not to be construed as analysis certificate or specifications.

Special Features
Shows broad processing window while providing good mechanical properties

Processing Conditions
Average extruder temperature range may be kept between 240 – 260°C.

Food Regulation
This product is defined as a preparation under specific food contact regulation. Detailed information will be provided in a relevant document “Regulatory Compliances Product Declaration” upon request.

Storage and Handling
Polypropylene resin should be stored to prevent a direct exposure to sunlight and heat. The Product estimated shelf life is one year starting from production date, adequate humidity below 80%, and temperature below 40°C. Customers might not fully follow the optimal storage condition, hence the shelf life recommended at customer site is six months only as received. Please refer to “Material Safety Datasheet” (MSDS) for handling and storage information.

Legal documents, MSDS, trial reports and machine builder certificate are available on request. Please send your request to the following e-mail: